MIL-W-22759/16
Application and Description
These ETFE insulated single-core MIL-W-22759/16 wires are used for MIL-Spec and Aerospace and other
applications requiring light weight, tight diameter tolerances, and enhanced mechanical toughness. ETFE
insulation also provides exceptional resistance to radiation and chemicals.
Construction Details
ETFE is extruded
Construction
Conductor: Tin plated copper
Insulation: Extruded ETFE
Insulating Material Thickness: 10 mil ( 0.25 mm)
Characteristics
Temperature Rating: 150°C
Voltage Rating: 600 volts
SAE AS22759/16
Color Code: MIL-STD-681
Dimensions and Weight
AWG
Size |
Conductor
Stranding |
Conductor
Oiam.
Min |
Conductor
Oiam.
Max |
Min O.D. |
Max O.D. |
Approx
LBS/
MFT |
|
|
In |
mm |
In |
mm |
In |
mm |
In |
mm |
|
24 |
19/36 |
0.023 |
0.584 |
0.024 |
0.610 |
0.043 |
1.092 |
0.047 |
1.194 |
2.4 |
22 |
19/34 |
0.029 |
0.737 |
0.031 |
0.787 |
0.050 |
1.270 |
0.054 |
1.372 |
3.52 |
20 |
19/32 |
0.037 |
0.940 |
0.039 |
0.991 |
0.058 |
1.473 |
0.062 |
1.575 |
5.18 |
18 |
19/30 |
0.046 |
1.168 |
0.049 |
1.245 |
0.069 |
1.753 |
0.073 |
1.854 |
7.65 |
16 |
19/29 |
0.052 |
1.321 |
0.055 |
1.397 |
0.077 |
1.956 |
0.081 |
2.057 |
9.68 |
14 |
19/27 |
0.065 |
1.651 |
0.069 |
1.753 |
0.091 |
2.311 |
0.095 |
2.413 |
14.5 |
12 |
37/28 |
0.087 |
2.210 |
0.089 |
2.261 |
0.111 |
2.819 |
0.117 |
2.972 |
21.8 |
10 |
37/26 |
0.106 |
2.692 |
0.112 |
2.845 |
0.136 |
3.454 |
0.142 |
3.607 |
34.0 |
8 |
133/29 |
0.158 |
4.013 |
0.169 |
4.293 |
0.196 |
4.978 |
0.202 |
5.131 |
61.5 |
6 |
133/27 |
0.198 |
5.029 |
0.212 |
5.385 |
0.247 |
6.274 |
0.253 |
6.426 |
96.9 |
4 |
133/25 |
0.250 |
6.350 |
0.268 |
6.807 |
0.308 |
7.823 |
0.316 |
8.026 |
152.0 |
2 |
665/30 |
0.320 |
8.128 |
0.340 |
8.636 |
0.384 |
9.754 |
0.392 |
9.957 |
231.0 |
1 |
817/30 |
0.360 |
9.144 |
0.380 |
9.652 |
0.426 |
10.820 |
0.436 |
11.074 |
314.0 |
2/0 |
1330/30 |
0.440 |
11.176 |
0.475 |
12.065 |
0.539 |
13.691 |
0.553 |
14.046 |
504.0 |
1/0 |
1045/30 |
0.395 |
10.033 |
0.425 |
10.795 |
0.473 |
12.014 |
0.485 |
12.319 |
391.0 |
|